New Generation Superplasticizing Admixtures

Nanoment® HP

High-Range Water Reducing / Superplasticizing Chemical Admixture for Concrete

Product Definition

Superplasticizing Chemical Admixture – Nanoment HP is a polycarboxylate based, high-range water reducer / superplasticizer type of chemical admixture for concrete. Nanoment HP permits a high reduction in water content of a given concrete compared to a reference concrete mixture without chemical admixture. Nanoment HP increases slump/flow of the mixture having the same amount of mixing water with the reference non-plasticized concrete.

Use

  • Nanoment HP is recommended for use in the applications below.
  • Heavily reinforced concrete structural sections requiring concrete mixtures with high workability and consistency classes.
  • Ready-Mixed concrete production requiring high plasticity and less workability loss.
  • In applications requiring broad-range concrete design for strength enhancement, improved workability and minimizing cement content.

Advantages and Properties

  • Nanoment HP provides more homogeneous distribution of cement particles mainly due to the steric effects of its side chains.
  • Reduces the agglomeration of cement particles and improves the flowability.
  • Provides significant increase in workability without increasing the quantity of mixing water and hence procures considerable convenience in mixing, transporting, placing and compaction of fresh concrete.
  • Improves the strength and durability by ensuring that the specified target consistency is achieved with lower water to binder ratios.
  • Provides high workability even in low water to binder ratios.
  • Nanoment HP is an appropriate type of admixture for concrete design aiming at reducing cement content to the allowed limits. High level of plasticizing capacity of Nanoment HP enables more economical concrete design with less cement content.
  • Concretes designed in this way may be beneficial with their lower shrinkage and heat of hydration characteristics.
    Enhances early strength as compared to a reference mixture having the same level of consistency without chemical admixture.
  • It is non-chloride admixture and does not contain any compounds that may cause corrosion
    of reinforcing steel.